Frit introduction
FRIT INTRODUCTION
Type | Item No | Description | COE | soft | Tempreture | A | B | C | D | E | F | Aplication |
Transparent |
DT215 | transparent | 215 | 650 | 950-1020℃ | O | O | O |
Double firing in fast kiln, Can modulate dolomite and waist line glaze, prevent peel of the glaze |
|||
DT185 | transparent | 185 | 650 | 950-1020℃ | O | O | O |
Double firing in fast kiln, Can modulate dolomite and waist line |
||||
DT165 | lead frit | 165 | 700 | 950-1050℃ | O | O | O | O | O | High brightness glaze which applied for traditional and fast firing kiln, Can bear high pressure | ||
DJ301 | transparent | 190 | 650 | 980-1020℃ | O | O | O |
Double firing in fast kiln, Can modulate dolomite and waist line |
||||
DG200 | lead frit | 195 | 750 | 950-1050℃ | O | O | O | O | O | Zn-Pb frit,Double firing and wide firing range, suitable for selenium glaze and waist line brick | ||
ST320 | High COE | 320 | 620 | 950-1000℃ | O | O | O | suitable for dolomite and cracking glaze, can act as flux for adjust the glaze COE. | ||||
ST155 | Low COE | 155 | 650 | 950-1000℃ | O | O | O | O | O | Double firing in fast kiln, can bear the high pressure and reduce the COE and protect cracking | ||
L201 | Low COE | 125 | 620 | 950-1020℃ | O | O | O | O | Can be matched with gloss glaze as well as added into glazes to reduce the COE | |||
High lead |
P2 | High lead | 220 | 400 | 650℃ | O | O | O | suitable for low-melting tile variable glaze ,print glaze and flux | |||
Zirconium white |
DKZ180 | Zirconium white | 180 | 700 | 950-1050℃ | O | O | O | O | good whiteness,low COE and wide firing range,can bear high pressure | ||
DKZ200 | Zirconium white | 200 | 655 | 950-1020℃ | O | O | O | O | O | high C.O.E and covering which suitable for the floor tiles with low firng point | ||
DKZ165 | Zirconium white | 165 | 800 | 1100-1200℃ | O | O | O | O | O | good whiteness,low COE and wide firing range,can bear high pressure | ||
DKZ300 | Zirconium white | 320 | 620 | 950-1020℃ | O | O | O | especially suitable for cracking frits | ||||
BO-3 |
bone china frit |
200 | 800 | 1100-1150℃ | O | O | O | O |
high brightness as well as for adjust the bone china glaze |
|||
K12 |
mid-melting frit |
198 | 850 | 1100-1180℃ | O | O | O | O | O | high brightness ,it favour development in color, and can adjust bone china glaze | ||
|
|